Product Detail
Mechanical Properties
| Property |
Testing Method |
Testing Condition |
Injection Molding Typical Value |
3D Printing X-Y Axis Typical Value |
3D Printing Z Axis Typical Value |
Unit |
| Tensile Strength |
ISO 527 |
50mm/min |
65.1 |
59±4 |
27±4 |
MPa |
| Elongation at Break |
ISO 527 |
50mm/min |
3.6 |
2±1 |
1.1±0.2 |
% |
| Tensile Modulus |
ISO 527 |
50mm/min |
2592.1 |
2207±200 |
1863.7±200 |
MPa |
| Flexural Strength |
ISO 178 |
2mm/min |
110.6 |
108.4±5 |
50.2±5 |
MPa |
| Flexural Modulus |
ISO 178 |
2mm/min |
2560 |
2335±200 |
1673.4±200 |
MPa |
| Charpy Impact Strength |
ISO 179 |
23℃ |
37.2 |
10.4±2 |
3.3±1 |
KJ/㎡ |
| Izod Impact Strength |
ISO 180 |
23℃ |
33.1 |
8.6±2 |
2.1±1 |
KJ/㎡ |
Physical Properties
| Property |
Testing Method |
Testing Condition |
Typical Value |
Unit |
| Density |
ISO 1183 |
Immersion |
1.13 |
g/cm3 |
| Melt Flow index(MFR) |
ISO 1133 |
275℃/2.16kg |
8-18 |
g/10 min |
Moisture Absorption
| Property |
Testing Method |
Testing Condition |
Injection Molding Typical Value |
3D Printing Typical Value |
Unit |
| Moisture Absorption |
ISO 62 |
50%RH*23℃ |
2.5 |
2.7 |
% |
Chemical Properties
| Property |
Testing Result |
| Weak Acid Resistance |
Not Resistant |
| Strong Acid Resistance |
Not Resistant |
| Weak Base Resistance |
Lightly Resistant |
| Strong Base Resistance |
Not Resistant |
| Organic Solution Resistance |
Not Resistant |
| Oil and Grease Resistance |
Resistant |
Thermal Properties
| Property |
Testing Method |
Testing Condition |
Injection Molding Typical Value |
3D Printing X-Y Axis Typical Value |
3D Printing Z Axis Typical Value |
Unit |
| Glass Transition Temperature |
DSC |
10℃/min |
53.7 |
℃ |
| Crystallization temperature |
DSC |
10℃/min |
179.8 |
℃ |
| Melting Point |
DSC |
10℃/min |
221.9 |
℃ |
| Distortion Temperature |
TGA |
20℃/min |
＞370 |
℃ |
| Heat Distortion Temperature |
ISO 75 |
0.45MPa |
72.8 |
69.7 |
57.4 |
℃ |
| Heat Distortion Temperature |
ISO 75 |
1.8MPa |
62.5 |
59.2 |
50.6 |
℃ |
| Vicat Softening Temperature |
ISO 306 |
50℃/10N |
N/A |
℃ |
Recommended 3D Printing Parameters*Based on 0.4 mm nozzle. Printing conditions may vary with different nozzle diameters.
| Printing Temperature |
250-280(℃) |
| Bed Temperature |
80-100(℃) |
| Wall Layers |
2 Layers |
| Top and Bottom Layers |
4 Layers |
| Infill |
100% |
| Ambient Temperature |
25℃ |
| Cooling Fan |
0-10% |
| Printing Speed |
30-50(mm/s) |
| Nozzle Diameter |
0.4 mm |
3D Printing Actual Parameters*All specimens must be left at room temperature for 24 hours before testing. The parameters are based on the Bambulab P1S 3D printer.
| Printing Temperature |
260(℃) |
| Bed Temperature |
80(℃) |
| Wall Layers |
2 Layers |
| Top and Bottom Layers |
4 Layers |
| Infill |
100% |
| Ambient Temperature |
25℃ |
| Cooling Fan |
10% |
| Printing Speed |
50(mm/s) |
| Nozzle Diameter |
0.4 mm |